pn

　　deion

　　adhesion (1)

　　adhesion (2)

　　1020r

　　ultraviolet film (pvc), 95 microns thick (3.8 mils), supplied in

　　100 meter (330') rolls with backing (typical use - wafer

　　backgrinding or dicing) (note: very high adhesive strength

　　to begin with, desirable for dicing operations, then reduces to a very low adhesive strength level after exposure to uv light,

　　ideal for pick and place operations)

　　@30 mins

　　(si) 375/20*

　　@24 hours

　　(si) 308/14*

　　@30 mins

　　(si) 320/15*

　　@24 hours

　　(si) 247/12*

　　1027r

　　super-high tack anti-static ultraviolet film (poly olefin) of 175 microns thick in 100 meter (330') rolls with pet backing

　　(typical use is for backgrinding or dicing)

　　@30 mins

　　(si) 1850/28*

　　@24 hours

　　(si) 1980/33*

　　@30 mins

　　(si)2080/28*

　　@24 hours

　　(si)2160/33*

　　1042r

　　anti-static ultraviolet film (poly olefin) of 98 microns thick in

　　100 meter (330') rolls with polyester backing (typical use is

　　for thin wafer dicing)

　　@30 mins

　　(si) 300/25*

　　@24 hours

　　(si) 550/28*

　　@30 mins

　　(si) 300/10*

　　@24 hours

　　(si) 600/10*

　　1043r

　　anti-static ultraviolet film (poly olefin) of 168 microns thick in

　　100 meter (330') rolls with polyester backing (typical use is

　　for thin wafer dicing)

　　@30 mins

　　(si) 890/20*

　　@24 hours

　　(si) 1042/60*

　　@30 mins

　　(si)1035/15*

　　@24 hours

　　(si)1105/28*

　　1044r

　　anti-static ultraviolet film (poly olefin) of 268 microns thick in

　　100 meter (330') rolls with polyester backing (typical use is

　　for thin wafer dicing)

　　@30 mins

　　(si) 350/29*

　　@24 hours

　　(si) 650/35*

　　@30 mins

　　(si) 400/15*

　　@24 hours

　　(si) 700/15*