產品說明Product description

·ES8002E是一款以SEBS為主基材的半透明材料，具有優異的耐刮擦效果和特別舒適的手感，強度高，成型快。

·ES8002E is a kind of translucent material with SEBS as major base material,it has very excellent scratch resistance,high strength and special comfortable touch feeling.Also it can be taken shape rapidly.

關鍵特性Key characteristic

1. 表面啞，手感細膩柔軟   dumb surface,soft and exquisite touch feeling
2. 高強度，成型快         high strength and rapid molding
3. 耐溫，耐候性能好       excellent temperature resistance and weather resistance
4. 可以包膠PP PE         It can be spliced with PP and PE.   

功能Function

產品應用

Main application

1運動器材Sports equipment

電子產品Electronic products

2汽車用品Auto parts

玩具產品Toy products

加工方法Processing method

注塑成型Injection molding

環保認證

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

顏色Color

透明Transparent

氣味Smell

少許樹脂味A little resin smell

外型Appearance

圓球形小顆粒Cylindrical particle，about 3mm×1.5mm

儲藏期Storage period

常溫下通風干燥，24個月Ventilated dry at normal temperature，about 24 months

包裝方式Packaging method

25公斤/袋 25kg/bag

物理性能Physical properties

結果Result

單位Unit

方法Method

成型條件Molding condition

比重Specific gravity

0.9±0.02

g/cm3

ASTM D792

干燥溫度Drying temp       90℃

硬度Hardness

80±5

shoreA

ASTM D2240

干燥時間Drying time     3Hours

拉伸強度Tensile strength

>5

Mpa

ASTM D412

射嘴溫度Nozzle temp      200℃

斷裂延伸Elongation at break

>500

%

ASTM D412

螺筒一段溫度Screw 1 temp 200℃

撕裂強度Tearing strength

>35

Kn/m

ASTM D624

螺筒二段溫度Screw 2 temp 190℃

熔融指數Melt index

>6

g/10min

ASTM D1238

螺筒三段溫度Screw 3 temp 180℃

注意事項Matters need attention

清洗料管

Purge compound

需使用PP或 PE清洗干凈機臺螺桿，且把機臺射嘴清除干凈please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean

著色

Coloring

請選擇以PE或EVA為基材之色母，切勿使用以PVC為基材者。另外加工時請采用較高的螺桿轉速和較高的背壓，才能讓著色劑達到較好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure and needed for better colorant dispersion

回收

Recycling

二次料（水口料）回收比率建議最多20%。

Consistent regrind usage of up to 20% is permissible